a淀粉的性能特點(diǎn) THE PERFORMANCE CHARACTERISTICS OF A-STARCH INCLUDE

能夠提高型砂的熱濕拉強(qiáng)度增加型砂韌性和鑄件模型表面光潔度、型砂表面的a淀粉受熱 燃燒后產(chǎn)生空隙，可以緩沖硅砂受熱膨脹。從而大大提高型砂的抗夾砂能力。

The  addition  of  a-starch  to   foundry  sand  can  enhance  its  thermal-wet  tensile  strength, increase  sand  toughness,and  improve  the  surface  finish  of  casting   molds.When  heated, the   a-starch   on   the    sand   surface    combusts   and    forms   voids,which   can   buffer   the  expansion  of  silica   sand.This  significantly  enhances  the  sand's  anti-sand-sticking  ability.

● 能夠降低型砂與模樣之間的磨擦阻力，提高型砂的起模性，減少由于起模不良而出現(xiàn)的 型廢率有效的減少了鑄件出現(xiàn)的缺陷問題。

The  addition  of  a-starch  to  foundry  sand  can  reduce  friction  between  the  sand  and  the pattern,enhancing  sand  mold  release  and  reducing  the  rate  of  sand  waste  due  to  poor    release.This   effectively   minimizes   defects   in   castings.

先進(jìn)的加工工藝(晶體膨脹熱熔)

● 如果濕砂型在合型以前放置一段時間，型砂表面失水而致表面強(qiáng)度下降和容易磨損，

澆注金屬液時易被沖蝕。放置時間較長或者天氣較干燥時，問題更為嚴(yán)重。型砂中加入龍祥 a淀粉可以提高型砂的抗風(fēng)干能力，減少鑄件沖砂缺陷。

If green  sand  molds  are  left  standing  before  closing  the  mold,the  surface  of  the  sand  may

lose  moisture,resulting  in  reduced  surface  strength  and  increased  wear.During  metal  pouring,   hese weakened areas are prone to erosion.This issue is more  severe with  longer  standing times or  in  dry  conditions.Adding  Longxiang  a-starch  to  the  foundry  sand  can  enhance  its  resistance to  drying  and  reduce  the   occurrence   of  sand-washing  defects  in  castings.

●a 淀粉的物理指標(biāo) The physical properties of A-starch are as follows  水分小于8%,水溶性大于90%,灰份小于0.5%,粒度(100目通過率)大于95%

執(zhí)行技術(shù)標(biāo)準(zhǔn) Technical    standards    compliance.